Type: Pool
Products Type: Plexiglass Sheet
Materials: Pmma, Acrylic
Packing: Both Sides Covered By Pe Film Or Craft Paper
Brand Name: Jinsui
Thickness: 20mm - 300mm
Place Of Origin: Jiangsu, China
Density: 1.20g/Cm3
Resistant: Excellent Resistance to Weather
Light Transmission: High Light Transmission (93%)
Process: Laser Engraving, CNC, Thermoforming
تفاصيل التعبئة والتغليف: 1. تم تحريكه مع ورق حرفي أو فيلم PE على كل من الحجم 2. طن/ صينية ، يغطي فيلم العبوات على كل درج واستخدم منصات الحديد للحماية 3. 18-20 طن/ 20'GP ، إجمالي 10 صواني.
الدعم: 400 Long Ton/Long Tons per Month swimming pools acrylic
ميناء: Shanghai
الدفع نوع: L/C,T/T
إنكوترم: FOB,CIF,EXW
|
Material
|
Lucite Acrylic
|
|
Thickness
|
20-300mm customized
|
|
Color
|
Clear/transparent
|
|
Shape
|
Customer's Demand
|
|
Surface
|
High Surface Hardness
|
|
Light transmission
|
High light transmission(93%)
|
|
Packing
|
PE film masking on both sides,KT board and angle iron.
|
|
Application
|
undersea world, Oceanarium, Zoo, Luxurious hotels, Swimming pools and so on.
|
|
PROPERTIES
|
VALUES
|
RULES
|
|
Density
|
1.19 g/cm3
|
ISO 1183-1:2012 Method A
|
|
Rockwell Hardness
|
112L
|
ISO 2039-2:1999
|
|
Tensile Modulus
|
3150MPa
|
EN ISO 527:2012
|
|
Tensile Strength
|
80.0MPa
|
EN ISO 527:2012
|
|
Tensile Strain at Break
|
3.2%
|
EN ISO 527-1:2012
|
|
Water Absorption
|
0.20%
|
ISO 62:2008 Method 1
|
|
Total Luminous Transmittance
|
93.4%
|
ISO 13468-1:1996
|
|
Vicat Softening Temperature
|
105℃
|
ISO 306:2013 Method B50
|
|
Light Ageing Test- UV Exposure
|
Grey scale: 5
|
ISO 4892-3:2016 Cycle 1
|
|
Mean Coefficient of Linear Thermal Expansion
|
72×10-6 K-1
|
ISO 11359-1:2014
|
|
Compressive Stress at Yield
|
129MPa
|
EN ISO 604:2003
|
|
Flexural Strength
|
120MPa
|
ISO 178:2013
|
|
Compressive Yield Strength
|
111MPa
|
ASTM D695-15
|
|
Compressive Modulus
|
3450MPa
|
ASTM D695-15
|
|
Shear Strength
|
59.7MPa
|
ASTM D732-17
|
|
Deflection Temperature under Load
|
100.2℃
|
ASTM D648-18 Method B
|
|
Modulus Elasticity
|
2810MPa
|
ASTM D695-15
|